NYHP-7350 PA(X) 基板产品规格表 Specification Sheet for Laminate
| NYHP-7350 PA(X) 覆铜板 NYHP-7350 PA(X) Type Laminate | 测试方法 Test Method | 测试条件 Test Condition | 单位Units | 典型值 Typical Value | |
| IPC-TM-650 | Metric(English) | 1.016mm CCL | |||
| 剥离强度 Peel Strength | 2.4.8 | 1oz RTF | N/mm(lb/inch) | ＞0.8 (4.5) | |
| 体积电阻 Volume Resistivity | 2.5.17.1 | COND A | MΩ-cm Minimum | 1.0×1010 | |
| 表面电阻 Surface Resistivity | 2.5.17.1 | COND A | MΩ-cm Minimum | 5.1×109 | |
| 吸水率 Water Absorption | 2.6.2.1 | — | % Maximum | 0.08 | |
| 介电常数Dk Permittivity | 2.5.5.5 | 10 GHz/23℃ | — Maximum | 3.5 | |
| 介质损耗 Df Loss Tangent | 2.5.5.5 | 10 GHz/23℃ | — Maximum | 0.0029 | |
| TCDK | 2.5.5.5 | -50℃-150℃ | PPM/℃ | 48 | |
| 弯曲强度 Flexural Strength A. 纵向 Length direction B. 横向 Cross direction | 2.4.4 | RT | N/mm2 Minimum | 220 140 | |
| 热应力冲击 Thermal Stress A. 未蚀刻 Unetched B. 蚀刻 Etched | 2.4.13.1 | 288℃ | 10 sec at 288℃ | Pass Pass | |
| 耐燃性 Flame Resistance ( Laminate & Prepreg as laminated) | — | — | Rating | NA | |
| 玻璃态转换温度Tg Glass Transition Temperature | 2.4.24 | DMA | ℃ | >190 | |
| 热分解温度Td Decomposition Temperature | TD (5% wt loss) | — | ℃ | 400 | |
| 膨胀系数 CTE | X/Y-axis CTE (50-125℃) | 2.4.24 | TMA | PPM/℃ | 19/20 |
| Z-axis CTE (50 to 125 ℃) | 2.4.24 | TMA | PPM/℃ | 50 | |
| Z-axis CTE (50 to 260 ℃) | 2.4.24 | TMA | % | 2.40% | |
| 耐热性(除去铜箔) Thermal Resistance (Copper removed) A.T260 B.T288 C.T300 | 2.4.24.1 | — | Minutes Minutes Minutes | >120 > 60 > 60 | |
| 耐CAF性能 CAF Resistance | 2.6.25 | AABUS | Pass/Fail | Pass | |
| PIM | 800/1800/2600 MHz | 43dBm | dBc | <-158 | |